INCONEL® liga 600 UNS N06600/alloy600/W.Nr. 2.4816
Liga | element | C | Si | Mn | S | Ni | Cr | Fe | Cu |
Liga600 | Min |
|
|
|
| 72 | 14.0 | 6.0 |
|
Max | 0.15 | 0.5 | 1.0 | 0.015 |
| 17.0 | 10.0 | 0.5 |
Status Aolly | Saħħa tat-tensjoni Rm Mpa Min | Saħħa ta 'rendiment RP 0. 2 Mpa Min | Titwil A 5 % Min |
ittemprat | 241 | 552 | 30 |
Densitàg/ċm3 | Punt tat-tidwib℃ |
8.47 | 1354~1413 |
Virga, Bar,Ħażniet tal-Wajer u Forġa - ASTM B 166/ASME SB 166, ASTM B 564/ASME SB 564 u N-253, SAE/AMS 5665 u 5687
Pjanċa, Sheet u Strixxa- ASTM B 168/ASME SB 168, ASTM B 906/ASME SB 906, Każijiet tal-Kodiċi ASME 1827 u N-253,SAE/AMS 5540,
Pajp u Tubu- ASTM B 167/ASME SB 167, ASTM B 163/ASME SB 163, ASTM B 516/ASME SB 516, ASTM B 517/ASME SB 517, ASTM B 751/ASME SB 751, ASTM B 775/ASME 751, ASTM B 775/ASME, ASTM B 829/ASME SB 829,
Oħrajn -ASTM B 366/ASME SB 366, DIN 17742, ISO 4955A, AFNOR NC15Fe
Reżistenti għal firxa wiesgħa ta 'midja korrużiva.
Prattikament immuni għall-ikkrekkjar tal-korrużjoni tal-istress tal-jone tal-kloru
Mhux manjetiku
Proprjetajiet mekkaniċi eċċellenti
Saħħa għolja u weldjabbiltà tajba taħt firxa wiesgħa ta 'temperaturi